Nb-B-C thin films for electrical contact applications deposited by magnetron sputtering [Elektronisk resurs]

• The high wear resistance, high chemical inertness, and high electrical conductivity of magnetron-sputtered transition metal diborides make them a candidate material for sliding electrical contacts. However, their high hardness makes it difficult to penetrate surface oxides, resulting in a high electrical contact resistance. In this study, the authors have investigated how the contact resistance can be improved by the formation of softer Nb-B-C films. The Nb-B-C films were deposited by magnetron sputtering and shown to exhibit a nanocomposite microstructure consisting of nanocrystalline NbB2-x grains with a solid solution of C separated by an amorphous BCx phase. The formation of the BCx phase reduces the hardness from 41 GPa for the NbB2-x film to 19 GPa at 36 at. % C. As a consequence the contact resistance is drastically reduced and the lowest contact resistance of 35 m Omega (contact force 5N) is achieved for a film containing 30 at. % C. However, crack formation and subsequent delamination and fragmentation is observed for the C-containing Nb-B-C films in tribology tests resulting in high friction values for these films. 

Ämnesord

Natural Sciences  (hsv)

Physical Sciences  (hsv)

Naturvetenskap  (hsv)

Fysik  (hsv)