Herein we report on the synthesis of a new layered ternary carbide, Mo2TiAlC2, that was synthesized by heating an elemental mixture at 1600 degrees C for 4 h under an Ar flow. Its hexagonal, a and c lattice parameters were calculated via Rietveld analysis of powder X-ray diffraction patterns to be, respectively, 2.997 angstrom and 18.661 angstrom. High-resolution scanning transmission electron microscopy showed that this phase is ordered, with Ti layers sandwiched between two Mo layers in a M(3)AX(2) type ternary carbide structure. (C) 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.