Effect of retained austenite on adhesion-dominated wear of nanostructured carbide-free bainitic steel [Elektronisk resurs]
-
Moghaddam, P. Valizadeh (författare)
-
Hardell, J. (författare)
-
Vuorinen, Esa, 1956- (författare)
-
Prakash, Braham (författare)
-
Luleå tekniska universitet Institutionen för teknikvetenskap och matematik (utgivare)
-
Luleå tekniska universitet Institutionen för teknikvetenskap och matematik (utgivare)
- Publicerad: Elsevier, 2020
- Engelska.
-
Ingår i: Tribology International. - 0301-679X. ; 150
-
Läs hela texten
-
Läs hela texten
-
Läs hela texten
- Relaterad länk:
-
http://www.ltu.se/ (Värdpublikation)
Sammanfattning
Ämnesord
Stäng
- Sliding wear performance of carbide-free bainitic steel is significantly affected by microstructure. This investigation is an attempt to find a correlation between microstructure and wear resistance of carbide-free bainitic steel and compare the results with that of a conventional tempered martensitic microstructure. Under predominantly adhesive wear conditions, carbide-free bainitic microstructure with the highest amount of retained austenite offers the best wear resistance. This is mainly attributed to the more pronounced work hardening and TRIP-effect of carbide-free bainitic microstructure austempered at higher temperature. Therefore, higher initial bulk hardness is not the only indicator of wear resistance. Moreover, when both oxidation and adhesion are active, a microstructure with an optimum content of retained austenite and bainitic ferrite shows the highest wear resistance.
Ämnesord
- Engineering and Technology (hsv)
- Mechanical Engineering (hsv)
- Tribology (Interacting Surfaces including Friction, Lubrication and Wear) (hsv)
- Teknik och teknologier (hsv)
- Maskinteknik (hsv)
- Tribologi (ytteknik omfattande friktion, nötning och smörjning) (hsv)
- Engineering and Technology (hsv)
- Materials Engineering (hsv)
- Other Materials Engineering (hsv)
- Teknik och teknologier (hsv)
- Materialteknik (hsv)
- Annan materialteknik (hsv)
- Machine Elements (ltu)
- Maskinelement (ltu)
- Engineering Materials (ltu)
- Materialteknik (ltu)
Genre
- government publication (marcgt)
Indexterm och SAB-rubrik
- bainite
- Carbide-free
- Retained austenite
- Wear
Inställningar
Hjälp
Ingår i annan publikation. Gå till titeln
Tribology International