High temperature phase decomposition in Ti x Zr y Al z N [Elektronisk resurs]
-
Lind, Hans (författare)
-
- Pilemalm, Robert, 1983- (författare)
-
-
Alternativt namn: Pilemalm, Robert K.M. 1983-
-
Alternativt namn: Pilemalm, Robert Kjell Mika, 1983-
-
Rogström, Lina (författare)
-
Tasnadi, Ferenc (författare)
-
Ghafoor, Naureen, 1975- (författare)
-
Forsén, Rikard, 1985- (författare)
-
Johnson, Lars (författare)
-
Jöesaar, Mats (författare)
-
Odén, Magnus (författare)
-
Abrikosov, Igor (författare)
-
Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
-
Linköpings universitet Tekniska högskolan (utgivare)
-
Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
- Publicerad: American Institute of Physics (AIP, 2014
- Engelska.
-
Ingår i: AIP Advances. - 2158-3226. ; 4:12, 127147-1-127147-9
-
Läs hela texten
-
Läs hela texten
-
Läs hela texten
Sammanfattning
Ämnesord
Stäng
- Through a combination of theoretical and experimental observations we study the high temperature decomposition behavior of c-(Ti x Zr y Al z N) alloys. We show that for most concentrations the high formation energy of (ZrAl)N causes a strong tendency for spinodal decomposition between ZrN and AlN while other decompositions tendencies are suppressed. In addition we observe that entropic effects due to configurational disorder favor a formation of a stable Zr-rich (TiZr)N phase with increasing temperature. Our calculations also predict that at high temperatures a Zr rich (TiZrAl)N disordered phase should become more resistant against the spinodal decomposition despite its high and positive formation energy due to the specific topology of the free energy surface at the relevant concentrations. Our experimental observations confirm this prediction by showing strong tendency towards decomposition in a Zr-poor sample while a Zr-rich alloy shows a greatly reduced decomposition rate, which is mostly attributable to binodal decomposition processes. This result highlights the importance of considering the second derivative of the free energy, in addition to its absolute value in predicting decomposition trends of thermodynamically unstable alloys.