  • Amiandamhen, Stephen,1983- (författare)

Effect of wood particle geometry and pre-treatments on the strength and sorption properties of cement-bonded particle boards [Elektronisk resurs]

  • E-artikel/E-kapitelEngelska2013

Förlag, utgivningsår, omfång ...

  • Publicerad:Applied and Natural Science Foundation,Publicerad:2013
  • rordacarrierrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:r2pb9vs1pmlrmnhk
  • http://urn.kb.se/resolve?urn=urn:nbn:se:lnu:diva-81157uri
  • urn:nbn:se:lnu:diva-81157urn

Kompletterande språkuppgifter

  • Språk:engelska

Ingår i deldatabas

Anmärkningar

  • Published
  • gratis
  • The effect of particle geometry and pretreatments on the strength and sorption properties of wood particlecement composite boards was investigated. Wood particles (flakes and sawdust) of Gmelina arborea were mixedwith cement and water in the production of composite boards. The wood particles were pretreated with hot water,calcium chloride and a combination of both treatments to enhance bonding with cement. The slurry was poured intorectangular moulds for board formation. After demoulding, the boards formed were tested for modulus of rupture(MOR), modulus of elasticity (MOE), water absorption (WA) and thickness swelling (TS). The results revealed thatthe mean MOR for flakes boards was 3.23N mm-2 while the mean MOR for sawdust boards was 3.01N mm-2. Hotwater and calcium chloride treatment produced the best effect in flake composite boards with MOR and MOE valuesof 6.90 N/mm2 and 1897.36 N mm-2 while sawdust composite boards had mean MOR and MOE values of 5.69Nmm-2 and 1664.31N mm-2 respectively. The WA rate after 24 hours of flakes and sawdust boards treated with hotwater and calcium chloride was 3.63% and 4.28% while the TS rate was 0.69% and 1.44% respectively. Particlegeometry and pretreatments significantly improved strength and sorption properties of wood particle cementcomposite boards (p<0.05).

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Izekor, David (författare)
  • GoFP (medarbetare)

Sammanhörande titlar

  • Del av/supplement till:channel record
  • Ingår i:Värdpublikation5:2, 318-322
  • Ingår i:VärdpublikationJournal of Applied and Natural Science5:2, 318-3220974-9411
  • Ingår i:Värdpublikation

Internetlänk

Inställningar Hjälp

Beståndsinformation saknas

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy