Synthesis, structural characterization and photocatalytic application of ZnO@ZnS core-shell nanoparticles [Elektronisk resurs]

Sadollahkhani, Azar (författare)
Kazeminezhad, Iraj (författare)
Lu, Jun (författare)
Nur, Omer (författare)
Hultman, Lars (författare)
Willander, Magnus (författare)
Linköpings universitet Institutionen för teknik och naturvetenskap (utgivare)
Alternativt namn: ITN
Alternativt namn: Linköping University. Department of Science and Technology
Linköpings universitet Tekniska högskolan (utgivare)
Alternativt namn: Linköpings universitet. Tekniska fakulteten
Alternativt namn: Linköpings tekniska högskola
Alternativt namn: Tekniska högskolan vid Linköpings universtiet
Alternativt namn: LiTH
Alternativt namn: Linköping University. Institute of Technology
Se även: Universitet i Linköping Tekniska högskolan
Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik (tidigare namn)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik, biologi och kemi (tidigare namn)
Alternativt namn: IFM
Alternativt namn: Engelska : Department of Physics and Measurement Technology, Biology and Chemistry
Alternativt namn: Engelska : Department of Physics, Chemistry and Biology
Royal Society of Chemistry 2014
Engelska.
Ingår i: RSC Advances. - 2046-2069. ; 4:70, 36940-36950
Läs hela texten
Läs hela texten
Läs hela texten
  • E-artikel/E-kapitel
Sammanfattning Ämnesord
Stäng  
  • ZnO nanoparticles were synthesized by co-precipitation with no capping agent followed by covering with ZnS using a solution-based chemical method at low temperature. By variation of the solution concentrations it was found that the fully-covering ZnS shell forms by a reaction of Na2S with ZnO NPs followed by the formation of ZnS nano-crystals by the reaction of Na2S with ZnCl2. The mechanism that led to full coverage of the ZnO core is proposed to be the addition of ZnCl2 at a later stage of the growth which guarantees a continuous supply of Zn ions to the core surface. Moreover, the ZnS nanocrystals that uniformly cover the ZnO NPs show no epitaxial relationship between the ZnO core and ZnS shell. The slow atomic mobility at the low reaction temperature is attributed to the non-epitaxial uniform ZnS shell growth. The rough surface of the ZnO grains provides initial nucleation positions for the growth of the ZnS shell nano-crystals. The low growth temperature also inhibits the abnormal growth of ZnS grains and results in the homogeneous coverage of ZnS nano-crystals on the ZnO core surface. The as-synthesized ZnO@ZnS core-shell nanoparticles were used as a photocatalyst to decompose Rose Bengal dye at three different pH values. ZnO@ZnS core-shell nanoparticles perform as a more active photocatalyst at a pH of 4, while pure ZnO nanoparticles are more efficient at a pH of 7. 

Ämnesord

Natural Sciences  (hsv)
Physical Sciences  (hsv)
Naturvetenskap  (hsv)
Fysik  (hsv)
Engineering and Technology  (hsv)
Electrical Engineering, Electronic Engineering, Information Engineering  (hsv)
Teknik och teknologier  (hsv)
Elektroteknik och elektronik  (hsv)
Inställningar Hjälp

Beståndsinformation saknas

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy