Structure and composition of silicon nitride and silicon carbon nitride coatings for joint replacements [Elektronisk resurs]

Pettersson, Maria (författare)
Berlind, Torun 1965- (författare)
Schmidt, Susann (författare)
Jacobsson, Staffan (författare)
Hultman, Lars (författare)
Persson, Cecilia (författare)
Engqvist, Håkan (författare)
Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik (tidigare namn)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik, biologi och kemi (tidigare namn)
Alternativt namn: IFM
Alternativt namn: Engelska : Department of Physics and Measurement Technology, Biology and Chemistry
Alternativt namn: Engelska : Department of Physics, Chemistry and Biology
Linköpings universitet Tekniska högskolan (utgivare)
Alternativt namn: Linköpings universitet. Tekniska fakulteten
Alternativt namn: Linköpings tekniska högskola
Alternativt namn: Tekniska högskolan vid Linköpings universtiet
Alternativt namn: LiTH
Alternativt namn: Linköping University. Institute of Technology
Se även: Universitet i Linköping Tekniska högskolan
Linköpings universitet Institutionen för fysik, kemi och biologi (utgivare)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik (tidigare namn)
Alternativt namn: Linköpings universitet. Institutionen för fysik och mätteknik, biologi och kemi (tidigare namn)
Alternativt namn: IFM
Alternativt namn: Engelska : Department of Physics and Measurement Technology, Biology and Chemistry
Alternativt namn: Engelska : Department of Physics, Chemistry and Biology
Elsevier 2013
Engelska.
Ingår i: Surface & Coatings Technology. - 0257-8972. ; 235:25, 827-834
Läs hela texten
Läs hela texten
Läs hela texten
  • E-artikel/E-kapitel
Sammanfattning Ämnesord
Stäng  
  • SiN x and SiC x N y coatings were fabricated with high power impulse magnetron sputtering (HiPIMS). The coatings microstructure, growth pattern, surface morphology, composition, and bonding structure were investigated by AFM, SEM, GIXRD, TEM, EDS as well as XPS, and related to the deposition parameters target powers and substrate temperature. Cross-sections of SiC x N y coatings showed either dense and laminar, or columnar structures. These coatings varied in roughness (Ra between 0.2 and 3.8 nm) and contained up to 35 at.% C. All coatings were substoichiometric (with an N/Si ratio from 0.27 to 0.65) and contained incorporated particles (so called droplets). The SiN x coatings, in particular those deposited at the lower power on the silicon target, demonstrated a dense microstructure and low surface roughness (Ra between 0.2 and 0.3 nm). They were dominated by an (X-ray) amorphous structure and consisted mainly of Si–N bonds. The usefulness of these coatings is discussed for bearing surfaces for hip joint arthroplasty in order to prolong their life-time. The long-term aim is to obtain a coating that reduces wear and metal ion release, that is biocompatible, and with wear debris that can dissolve in vivo . 

Ämnesord

Engineering and Technology  (hsv)
Teknik och teknologier  (hsv)

Indexterm och SAB-rubrik

Silicon nitride coating; Silicon carbon nitride coating; High power impulse magnetron sputtering (HIPIMS); Total joint replacements; Microstructure
Inställningar Hjälp

Beståndsinformation saknas

Om LIBRIS
Sekretess
Blogg
Hjälp
Fel i posten?
Kontakt
Teknik och format
Sök utifrån
Sökrutor
Plug-ins
Bookmarklet
Anpassa
Textstorlek
Kontrast
Vyer
LIBRIS söktjänster
SwePub
Sondera
Uppsök

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

Copyright © LIBRIS - Nationella bibliotekssystem

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy